ASTM A369 Grade FP5 vs. S44700 Stainless Steel

Both ASTM A369 grade FP5 and S44700 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 73% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is S44700 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
200
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 20
23
Fatigue Strength, MPa 160
300
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 74
82
Shear Strength, MPa 300
380
Tensile Strength: Ultimate (UTS), MPa 470
600
Tensile Strength: Yield (Proof), MPa 240
450

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Maximum Temperature: Mechanical, °C 510
1100
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 13
11

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
18
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
3.6
Embodied Energy, MJ/kg 23
49
Embodied Water, L/kg 69
180

Common Calculations

PREN (Pitting Resistance) 6.8
42
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
120
Resilience: Unit (Modulus of Resilience), kJ/m3 140
480
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
21
Strength to Weight: Bending, points 17
20
Thermal Shock Resistance, points 13
19

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.010
Chromium (Cr), % 4.0 to 6.0
28 to 30
Copper (Cu), % 0
0 to 0.15
Iron (Fe), % 92.1 to 95.3
64.9 to 68.5
Manganese (Mn), % 0.3 to 0.6
0 to 0.3
Molybdenum (Mo), % 0.45 to 0.65
3.5 to 4.2
Nickel (Ni), % 0
0 to 0.15
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.2
Sulfur (S), % 0 to 0.025
0 to 0.020