ASTM A369 Grade FP92 vs. EN 1.4981 Stainless Steel

Both ASTM A369 grade FP92 and EN 1.4981 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP92 and the bottom bar is EN 1.4981 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
39
Fatigue Strength, MPa 330
210
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 440
420
Tensile Strength: Ultimate (UTS), MPa 710
610
Tensile Strength: Yield (Proof), MPa 490
240

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Maximum Temperature: Mechanical, °C 590
940
Melting Completion (Liquidus), °C 1490
1440
Melting Onset (Solidus), °C 1450
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 26
16
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.3
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 10
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 11
25
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 2.8
4.8
Embodied Energy, MJ/kg 40
67
Embodied Water, L/kg 89
150

Common Calculations

PREN (Pitting Resistance) 14
22
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
190
Resilience: Unit (Modulus of Resilience), kJ/m3 620
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
21
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 6.9
4.3
Thermal Shock Resistance, points 19
14

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0010 to 0.0060
0
Carbon (C), % 0.070 to 0.13
0.040 to 0.1
Chromium (Cr), % 8.5 to 9.5
15.5 to 17.5
Iron (Fe), % 85.8 to 89.1
59.6 to 66.7
Manganese (Mn), % 0.3 to 0.6
0 to 1.5
Molybdenum (Mo), % 0.3 to 0.6
1.6 to 2.0
Nickel (Ni), % 0 to 0.4
15.5 to 17.5
Niobium (Nb), % 0.040 to 0.090
0.4 to 1.2
Nitrogen (N), % 0.030 to 0.070
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.5
0.3 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0 to 0.010
0
Tungsten (W), % 1.5 to 2.0
0
Vanadium (V), % 0.15 to 0.25
0
Zirconium (Zr), % 0 to 0.010
0