ASTM A372 Grade J Steel vs. AISI 201L Stainless Steel
Both ASTM A372 grade J steel and AISI 201L stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is ASTM A372 grade J steel and the bottom bar is AISI 201L stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 310 | |
| 190 to 320 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 17 to 22 | |
| 22 to 46 |
| Fatigue Strength, MPa | 310 to 570 | |
| 270 to 530 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 77 |
| Shear Strength, MPa | 410 to 630 | |
| 520 to 660 |
| Tensile Strength: Ultimate (UTS), MPa | 650 to 1020 | |
| 740 to 1040 |
| Tensile Strength: Yield (Proof), MPa | 430 to 850 | |
| 290 to 790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 880 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1410 |
| Melting Onset (Solidus), °C | 1420 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 44 | |
| 15 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 12 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 2.6 |
| Embodied Energy, MJ/kg | 20 | |
| 38 |
| Embodied Water, L/kg | 51 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 170 | |
| 210 to 300 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 500 to 1930 | |
| 220 to 1570 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 23 to 36 | |
| 27 to 37 |
| Strength to Weight: Bending, points | 21 to 29 | |
| 24 to 30 |
| Thermal Diffusivity, mm2/s | 12 | |
| 4.0 |
| Thermal Shock Resistance, points | 19 to 30 | |
| 16 to 23 |
Alloy Composition
| Carbon (C), % | 0.35 to 0.5 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0.8 to 1.2 | |
| 16 to 18 |
| Iron (Fe), % | 96.7 to 97.8 | |
| 67.9 to 75 |
| Manganese (Mn), % | 0.75 to 1.1 | |
| 5.5 to 7.5 |
| Molybdenum (Mo), % | 0.15 to 0.25 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 3.5 to 5.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.25 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.045 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |