ASTM A372 Grade J Steel vs. SAE-AISI 1137 Steel

Both ASTM A372 grade J steel and SAE-AISI 1137 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade J steel and the bottom bar is SAE-AISI 1137 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 310
200 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17 to 22
11 to 17
Fatigue Strength, MPa 310 to 570
250 to 400
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 410 to 630
430 to 460
Tensile Strength: Ultimate (UTS), MPa 650 to 1020
700 to 760
Tensile Strength: Yield (Proof), MPa 430 to 850
370 to 650

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
51
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
10
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
12

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.4
Embodied Energy, MJ/kg 20
19
Embodied Water, L/kg 51
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 170
81 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 500 to 1930
360 to 1130
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23 to 36
25 to 27
Strength to Weight: Bending, points 21 to 29
22 to 24
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 19 to 30
21 to 23

Alloy Composition

Carbon (C), % 0.35 to 0.5
0.32 to 0.39
Chromium (Cr), % 0.8 to 1.2
0
Iron (Fe), % 96.7 to 97.8
97.8 to 98.3
Manganese (Mn), % 0.75 to 1.1
1.4 to 1.7
Molybdenum (Mo), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.015
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0
Sulfur (S), % 0 to 0.010
0.080 to 0.13

Comparable Variants