MakeItFrom.com
Menu (ESC)

ASTM A387 Grade 11 Steel vs. ASTM A372 Grade J Steel

Both ASTM A387 grade 11 steel and ASTM A372 grade J steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 11 steel and the bottom bar is ASTM A372 grade J steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 180
200 to 310
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 25
17 to 22
Fatigue Strength, MPa 200 to 250
310 to 570
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 320 to 390
410 to 630
Tensile Strength: Ultimate (UTS), MPa 500 to 600
650 to 1020
Tensile Strength: Yield (Proof), MPa 270 to 350
430 to 850

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 430
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
44
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.5
Embodied Energy, MJ/kg 21
20
Embodied Water, L/kg 53
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100 to 130
130 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 200 to 320
500 to 1930
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18 to 21
23 to 36
Strength to Weight: Bending, points 18 to 20
21 to 29
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 15 to 18
19 to 30

Alloy Composition

Carbon (C), % 0.050 to 0.17
0.35 to 0.5
Chromium (Cr), % 1.0 to 1.5
0.8 to 1.2
Iron (Fe), % 96.2 to 97.6
96.7 to 97.8
Manganese (Mn), % 0.4 to 0.65
0.75 to 1.1
Molybdenum (Mo), % 0.45 to 0.65
0.15 to 0.25
Phosphorus (P), % 0 to 0.025
0 to 0.015
Silicon (Si), % 0.5 to 0.8
0.15 to 0.35
Sulfur (S), % 0 to 0.025
0 to 0.010

Comparable Variants