ASTM A414 Steel vs. SAE-AISI 1144 Steel
Both ASTM A414 steel and SAE-AISI 1144 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is ASTM A414 steel and the bottom bar is SAE-AISI 1144 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 110 to 180 | |
| 220 to 230 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 15 to 26 | |
| 11 to 17 |
| Fatigue Strength, MPa | 140 to 260 | |
| 280 to 430 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 72 |
| Shear Strength, MPa | 230 to 370 | |
| 460 to 510 |
| Tensile Strength: Ultimate (UTS), MPa | 360 to 590 | |
| 750 to 840 |
| Tensile Strength: Yield (Proof), MPa | 190 to 350 | |
| 420 to 690 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 49 to 50 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 to 7.3 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 to 8.4 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.2 | |
| 1.9 |
| Density, g/cm3 | 7.8 to 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 1.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 20 to 22 | |
| 19 |
| Embodied Water, L/kg | 48 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 69 to 130 | |
| 91 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 330 | |
| 480 to 1290 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 13 to 21 | |
| 27 to 30 |
| Strength to Weight: Bending, points | 14 to 20 | |
| 23 to 25 |
| Thermal Diffusivity, mm2/s | 13 | |
| 14 |
| Thermal Shock Resistance, points | 11 to 17 | |
| 22 to 24 |