ASTM B596 Au-Cu vs. AISI 410 Stainless Steel

ASTM B596 Au-Cu belongs to the otherwise unclassified metals classification, while AISI 410 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ASTM B596 Au-Cu and the bottom bar is AISI 410 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
190
Elongation at Break, % 4.3 to 17
16 to 22
Poisson's Ratio 0.41
0.28
Shear Modulus, GPa 36
76
Shear Strength, MPa 280 to 360
330 to 470
Tensile Strength: Ultimate (UTS), MPa 450 to 620
520 to 770

Thermal Properties

Latent Heat of Fusion, J/g 77
270
Melting Completion (Liquidus), °C 1060
1530
Melting Onset (Solidus), °C 930
1480
Specific Heat Capacity, J/kg-K 150
480
Thermal Expansion, µm/m-K 14
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 14
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 6.7
3.3

Otherwise Unclassified Properties

Density, g/cm3 18
7.7

Common Calculations

Stiffness to Weight: Axial, points 3.1
14
Stiffness to Weight: Bending, points 8.5
25
Strength to Weight: Axial, points 6.8 to 9.4
19 to 28
Strength to Weight: Bending, points 7.1 to 8.8
19 to 24
Thermal Shock Resistance, points 22 to 30
18 to 26

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.080 to 0.15
Chromium (Cr), % 0
11.5 to 13.5
Copper (Cu), % 9.0 to 11
0
Gold (Au), % 89 to 91
0
Iron (Fe), % 0
83.5 to 88.4
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0
0 to 0.75
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Residuals, % 0 to 0.4
0

Comparable Variants