ASTM B628 Ag-Cu vs. Grade VDSiCrV Steel

ASTM B628 Ag-Cu belongs to the otherwise unclassified metals classification, while grade VDSiCrV steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is ASTM B628 Ag-Cu and the bottom bar is grade VDSiCrV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
190
Poisson's Ratio 0.36
0.29
Shear Modulus, GPa 31
80
Tensile Strength: Ultimate (UTS), MPa 350 to 760
2100

Thermal Properties

Latent Heat of Fusion, J/g 140
270
Melting Completion (Liquidus), °C 780
1440
Melting Onset (Solidus), °C 780
1400
Specific Heat Capacity, J/kg-K 280
480
Thermal Expansion, µm/m-K 19
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 84
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 75
8.6

Otherwise Unclassified Properties

Density, g/cm3 10
7.7

Common Calculations

Stiffness to Weight: Axial, points 4.6
13
Stiffness to Weight: Bending, points 14
25
Strength to Weight: Axial, points 9.5 to 21
75
Strength to Weight: Bending, points 11 to 18
47
Thermal Shock Resistance, points 16 to 34
63

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0
Cadmium (Cd), % 0 to 0.050
0
Carbon (C), % 0
0.5 to 0.7
Chromium (Cr), % 0
0.5 to 1.0
Copper (Cu), % 26.6 to 29
0 to 0.060
Iron (Fe), % 0 to 0.050
96.1 to 97.8
Lead (Pb), % 0 to 0.030
0
Manganese (Mn), % 0
0.4 to 0.9
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0
1.2 to 1.7
Silver (Ag), % 71 to 73
0
Sulfur (S), % 0
0 to 0.020
Vanadium (V), % 0
0.1 to 0.25
Zinc (Zn), % 0 to 0.060
0
Residuals, % 0 to 0.21
0