ASTM B780 Alloy vs. AWS E630

ASTM B780 alloy belongs to the otherwise unclassified metals classification, while AWS E630 belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is ASTM B780 alloy and the bottom bar is AWS E630.

ASTM B780 Silver-Copper-Nickel Electrical Contact Alloy AWS E630 (W37410) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		83
Elastic (Young's, Tensile) Modulus, GPa		190

Elongation at Break, %		1.1 to 9.1
Elongation at Break, %		8.0

Poisson's Ratio		0.36
Poisson's Ratio		0.28

Shear Modulus, GPa		30
Shear Modulus, GPa		76

Tensile Strength: Ultimate (UTS), MPa		330 to 590
Tensile Strength: Ultimate (UTS), MPa		1040

Thermal Properties

Latent Heat of Fusion, J/g		140
Latent Heat of Fusion, J/g		280

Specific Heat Capacity, J/kg-K		270
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		18
Thermal Expansion, µm/m-K		14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		70 to 76
Electrical Conductivity: Equal Volume, % IACS		2.3

Electrical Conductivity: Equal Weight (Specific), % IACS		62 to 68
Electrical Conductivity: Equal Weight (Specific), % IACS		2.6

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		7.8

Common Calculations

Stiffness to Weight: Axial, points		4.5
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		14
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		9.1 to 16
Strength to Weight: Axial, points		37

Strength to Weight: Bending, points		11 to 15
Strength to Weight: Bending, points		29

Thermal Shock Resistance, points		16 to 29
Thermal Shock Resistance, points		28

Alloy Composition

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Carbon (C), %		0
Carbon (C), %		0 to 0.050

Chromium (Cr), %		0
Chromium (Cr), %		16 to 16.8

Copper (Cu), %		23.5 to 25.7
Copper (Cu), %		3.3 to 4.0

Iron (Fe), %		0 to 0.050
Iron (Fe), %		71.6 to 75.9

Lead (Pb), %		0 to 0.030
Lead (Pb), %		0

Manganese (Mn), %		0
Manganese (Mn), %		0.25 to 0.75

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0 to 0.75

Nickel (Ni), %		0.35 to 0.65
Nickel (Ni), %		4.5 to 5.0

Niobium (Nb), %		0
Niobium (Nb), %		0.15 to 0.3

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0
Silicon (Si), %		0 to 0.75

Silver (Ag), %		74 to 76
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030

Zinc (Zn), %		0 to 0.060
Zinc (Zn), %		0