ASTM Grade HE Steel vs. EN 1.0481 Steel

Both ASTM grade HE steel and EN 1.0481 steel are iron alloys. They have 62% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HE steel and the bottom bar is EN 1.0481 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
150
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 10
24
Fatigue Strength, MPa 160
210
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 670
510
Tensile Strength: Yield (Proof), MPa 310
300

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
50
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 19
2.2
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.5
1.5
Embodied Energy, MJ/kg 50
20
Embodied Water, L/kg 190
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 56
100
Resilience: Unit (Modulus of Resilience), kJ/m3 240
230
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
18
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 3.6
13
Thermal Shock Resistance, points 14
16

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 0.2 to 0.5
0.080 to 0.2
Chromium (Cr), % 26 to 30
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 53.9 to 65.8
96.8 to 99
Manganese (Mn), % 0 to 2.0
0.9 to 1.5
Molybdenum (Mo), % 0 to 0.5
0 to 0.080
Nickel (Ni), % 8.0 to 11
0 to 0.3
Niobium (Nb), % 0
0 to 0.020
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 2.0
0 to 0.4
Sulfur (S), % 0 to 0.040
0 to 0.010
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.020