MakeItFrom.com
Menu (ESC)

ASTM Grade HE Steel vs. EN 1.4002 Stainless Steel

Both ASTM grade HE steel and EN 1.4002 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HE steel and the bottom bar is EN 1.4002 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 10
19
Fatigue Strength, MPa 160
160
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
76
Tensile Strength: Ultimate (UTS), MPa 670
500
Tensile Strength: Yield (Proof), MPa 310
260

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 450
390
Maximum Temperature: Mechanical, °C 1100
760
Melting Completion (Liquidus), °C 1400
1440
Melting Onset (Solidus), °C 1360
1400
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
30
Thermal Expansion, µm/m-K 17
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 19
7.0
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 3.5
1.9
Embodied Energy, MJ/kg 50
27
Embodied Water, L/kg 190
100

Common Calculations

PREN (Pitting Resistance) 29
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 56
80
Resilience: Unit (Modulus of Resilience), kJ/m3 240
170
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24
18
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 3.6
8.1
Thermal Shock Resistance, points 14
18

Alloy Composition

Aluminum (Al), % 0
0.1 to 0.3
Carbon (C), % 0.2 to 0.5
0 to 0.080
Chromium (Cr), % 26 to 30
12 to 14
Iron (Fe), % 53.9 to 65.8
83.6 to 87.9
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 8.0 to 11
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015