ASTM Grade HE Steel vs. EN 1.4005 Stainless Steel

Both ASTM grade HE steel and EN 1.4005 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HE steel and the bottom bar is EN 1.4005 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 10
13 to 21
Fatigue Strength, MPa 160
240 to 290
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
76
Tensile Strength: Ultimate (UTS), MPa 670
630 to 750
Tensile Strength: Yield (Proof), MPa 310
370 to 500

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Corrosion, °C 450
390
Maximum Temperature: Mechanical, °C 1100
760
Melting Completion (Liquidus), °C 1400
1440
Melting Onset (Solidus), °C 1360
1400
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
30
Thermal Expansion, µm/m-K 17
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 19
7.0
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 3.5
2.0
Embodied Energy, MJ/kg 50
28
Embodied Water, L/kg 190
100

Common Calculations

PREN (Pitting Resistance) 29
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 56
90 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 240
350 to 650
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24
23 to 27
Strength to Weight: Bending, points 22
21 to 24
Thermal Diffusivity, mm2/s 3.6
8.1
Thermal Shock Resistance, points 14
23 to 27

Alloy Composition

Carbon (C), % 0.2 to 0.5
0.060 to 0.15
Chromium (Cr), % 26 to 30
12 to 14
Iron (Fe), % 53.9 to 65.8
82.4 to 87.8
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 0 to 0.5
0 to 0.6
Nickel (Ni), % 8.0 to 11
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.040
0.15 to 0.35