ASTM Grade HE Steel vs. EN 1.4530 Stainless Steel

Both ASTM grade HE steel and EN 1.4530 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HE steel and the bottom bar is EN 1.4530 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
76
Tensile Strength: Ultimate (UTS), MPa 670
1030 to 1370

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Corrosion, °C 450
450
Maximum Temperature: Mechanical, °C 1100
790
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1410
Specific Heat Capacity, J/kg-K 490
470
Thermal Expansion, µm/m-K 17
11

Otherwise Unclassified Properties

Base Metal Price, % relative 19
15
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.5
3.4
Embodied Energy, MJ/kg 50
46
Embodied Water, L/kg 190
130

Common Calculations

PREN (Pitting Resistance) 29
19
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24
36 to 48
Strength to Weight: Bending, points 22
29 to 35
Thermal Shock Resistance, points 14
35 to 47

Alloy Composition

Aluminum (Al), % 0
0.6 to 0.8
Carbon (C), % 0.2 to 0.5
0 to 0.015
Chromium (Cr), % 26 to 30
11.5 to 12.5
Iron (Fe), % 53.9 to 65.8
74.4 to 77.3
Manganese (Mn), % 0 to 2.0
0 to 0.1
Molybdenum (Mo), % 0 to 0.5
1.9 to 2.2
Nickel (Ni), % 8.0 to 11
8.5 to 9.5
Nitrogen (N), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.040
0 to 0.010
Silicon (Si), % 0 to 2.0
0 to 0.1
Sulfur (S), % 0 to 0.040
0 to 0.0050
Titanium (Ti), % 0
0.28 to 0.37