ASTM Grade HF Steel vs. EN 1.8523 Steel

Both ASTM grade HF steel and EN 1.8523 steel are iron alloys. They have 71% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HF steel and the bottom bar is EN 1.8523 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
300
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 29
15
Fatigue Strength, MPa 200
530
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
74
Tensile Strength: Ultimate (UTS), MPa 550
1000
Tensile Strength: Yield (Proof), MPa 270
800

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Maximum Temperature: Mechanical, °C 1000
480
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
39
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 17
4.2
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.2
2.2
Embodied Energy, MJ/kg 46
31
Embodied Water, L/kg 150
64

Common Calculations

PREN (Pitting Resistance) 21
6.4
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
140
Resilience: Unit (Modulus of Resilience), kJ/m3 180
1700
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
36
Strength to Weight: Bending, points 19
28
Thermal Diffusivity, mm2/s 4.2
10
Thermal Shock Resistance, points 12
29

Alloy Composition

Carbon (C), % 0.2 to 0.4
0.35 to 0.45
Chromium (Cr), % 18 to 23
3.0 to 3.5
Iron (Fe), % 60 to 73.8
93.5 to 95.7
Manganese (Mn), % 0 to 2.0
0.4 to 0.7
Molybdenum (Mo), % 0 to 0.5
0.8 to 1.1
Nickel (Ni), % 8.0 to 12
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 2.0
0 to 0.4
Sulfur (S), % 0 to 0.040
0 to 0.035
Vanadium (V), % 0
0.15 to 0.25