ASTM Grade HG10 MNN Steel vs. AWS E312

Both ASTM grade HG10 MNN steel and AWS E312 are iron alloys. They have 89% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HG10 MNN steel and the bottom bar is AWS E312.

ASTM Grade HG10 MNN (19Cr-12Ni-4Mn, J92604) Cast Stainless Steel AWS E312 (W31310) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		23
Elongation at Break, %		25

Poisson's Ratio		0.28
Poisson's Ratio		0.27

Shear Modulus, GPa		77
Shear Modulus, GPa		80

Tensile Strength: Ultimate (UTS), MPa		590
Tensile Strength: Ultimate (UTS), MPa		740

Thermal Properties

Latent Heat of Fusion, J/g		290
Latent Heat of Fusion, J/g		310

Melting Completion (Liquidus), °C		1420
Melting Completion (Liquidus), °C		1410

Melting Onset (Solidus), °C		1370
Melting Onset (Solidus), °C		1360

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		15

Otherwise Unclassified Properties

Base Metal Price, % relative		21
Base Metal Price, % relative		20

Density, g/cm³		7.8
Density, g/cm³		7.7

Embodied Carbon, kg CO₂/kg material		4.0
Embodied Carbon, kg CO₂/kg material		3.6

Embodied Energy, MJ/kg		58
Embodied Energy, MJ/kg		52

Embodied Water, L/kg		160
Embodied Water, L/kg		200

Common Calculations

PREN (Pitting Resistance)		25
PREN (Pitting Resistance)		31

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		15

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		21
Strength to Weight: Axial, points		27

Strength to Weight: Bending, points		20
Strength to Weight: Bending, points		24

Thermal Shock Resistance, points		13
Thermal Shock Resistance, points		18

Alloy Composition

Carbon (C), %		0.070 to 0.11
Carbon (C), %		0 to 0.15

Chromium (Cr), %		18.5 to 20.5
Chromium (Cr), %		28 to 32

Copper (Cu), %		0 to 0.5
Copper (Cu), %		0 to 0.75

Iron (Fe), %		57.9 to 66.5
Iron (Fe), %		52.3 to 63.5

Manganese (Mn), %		3.0 to 5.0
Manganese (Mn), %		0.5 to 2.5

Molybdenum (Mo), %		0.25 to 0.45
Molybdenum (Mo), %		0 to 0.75

Nickel (Ni), %		11.5 to 13.5
Nickel (Ni), %		8.0 to 10.5

Niobium (Nb), %		0.2 to 1.0
Niobium (Nb), %		0

Nitrogen (N), %		0.2 to 0.3
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0 to 0.7
Silicon (Si), %		0 to 1.0

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030