AWS BAg-10 belongs to the otherwise unclassified metals classification, while C92500 bronze belongs to the copper alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 15 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-10 and the bottom bar is C92500 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
110
Poisson's Ratio 0.35
0.34
Shear Modulus, GPa 30
40
Tensile Strength: Ultimate (UTS), MPa 140
310

Thermal Properties

Latent Heat of Fusion, J/g 130
190
Melting Completion (Liquidus), °C 740
980
Melting Onset (Solidus), °C 690
870
Specific Heat Capacity, J/kg-K 280
370
Thermal Expansion, µm/m-K 20
18

Otherwise Unclassified Properties

Density, g/cm3 9.8
8.7

Common Calculations

Stiffness to Weight: Axial, points 4.6
6.8
Stiffness to Weight: Bending, points 15
18
Strength to Weight: Axial, points 4.0
9.8
Strength to Weight: Bending, points 6.1
12
Thermal Shock Resistance, points 6.2
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Copper (Cu), % 19 to 21
85 to 88
Iron (Fe), % 0
0 to 0.3
Lead (Pb), % 0
1.0 to 1.5
Nickel (Ni), % 0
0.8 to 1.5
Phosphorus (P), % 0
0 to 1.5
Silicon (Si), % 0
0 to 0.0050
Silver (Ag), % 69 to 71
0
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0
10 to 12
Zinc (Zn), % 8.0 to 12
0 to 0.5
Residuals, % 0 to 0.15
0 to 0.7