AWS BAg-18 belongs to the otherwise unclassified metals classification, while EN 2.4856 nickel belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-18 and the bottom bar is EN 2.4856 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
200
Poisson's Ratio 0.36
0.29
Shear Modulus, GPa 30
79
Tensile Strength: Ultimate (UTS), MPa 170
880

Thermal Properties

Latent Heat of Fusion, J/g 130
330
Melting Completion (Liquidus), °C 720
1480
Melting Onset (Solidus), °C 600
1430
Specific Heat Capacity, J/kg-K 280
440
Thermal Expansion, µm/m-K 19
11

Otherwise Unclassified Properties

Density, g/cm3 9.7
8.6
Embodied Carbon, kg CO2/kg material 59
14
Embodied Energy, MJ/kg 930
190

Common Calculations

Stiffness to Weight: Axial, points 4.7
13
Stiffness to Weight: Bending, points 15
23
Strength to Weight: Axial, points 4.9
28
Strength to Weight: Bending, points 7.0
24
Thermal Shock Resistance, points 7.7
29

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.4
Carbon (C), % 0
0.030 to 0.1
Chromium (Cr), % 0
20 to 23
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 28.4 to 31.5
0 to 0.5
Iron (Fe), % 0
0 to 5.0
Manganese (Mn), % 0
0 to 0.5
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 0
58 to 68.8
Niobium (Nb), % 0
3.2 to 4.2
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 59 to 61
0
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 9.5 to 10.5
0
Titanium (Ti), % 0
0 to 0.4
Residuals, % 0 to 0.15
0