Menu (ESC)

AWS BAg-18 (P07600) Filler Metal

AWS BAg-18 is a silver-based filler metal for brazing. Cited properties are appropriate for the as-fabricated (no temper or treatment) condition. BAg-18 is the AWS designation for this material. P07600 is the UNS number.

It has a very low melting temperature among the silver-based braze fillers in the database.

The graph bars on the material properties cards below compare AWS BAg-18 to: silver-based braze fillers (top), all alloys in the same category (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

82 GPa 12 x 106 psi

Poisson's Ratio


Shear Modulus

30 GPa 4.4 x 106 psi

Tensile Strength: Ultimate (UTS)

170 MPa 25 x 103 psi

Thermal Properties

Brazing Temperature

720 to 980 °C 1320 to 1800 °F

Latent Heat of Fusion

130 J/g

Melting Completion (Liquidus)

720 °C 1320 °F

Melting Onset (Solidus)

600 °C 1120 °F

Specific Heat Capacity

280 J/kg-K 0.067 BTU/lb-°F

Thermal Expansion

19 µm/m-K

Otherwise Unclassified Properties


9.7 g/cm3 610 lb/ft3

Embodied Carbon

59 kg CO2/kg material

Embodied Energy

930 MJ/kg 400 x 103 BTU/lb

Common Calculations

Stiffness to Weight: Axial

4.7 points

Stiffness to Weight: Bending

15 points

Strength to Weight: Axial

4.9 points

Strength to Weight: Bending

7.0 points

Thermal Shock Resistance

7.7 points

Alloy Composition

Silver (Ag)Ag 59 to 61
Copper (Cu)Cu 28.4 to 31.5
Tin (Sn)Sn 9.5 to 10.5
Residualsres. 0 to 0.15

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

AWS A5.8: Specification for Filler Metals for Brazing and Braze Welding