AWS BAg-18 vs. Grade CZ100 Nickel

AWS BAg-18 belongs to the otherwise unclassified metals classification, while grade CZ100 nickel belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-18 and the bottom bar is grade CZ100 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
180
Poisson's Ratio 0.36
0.31
Shear Modulus, GPa 30
69
Tensile Strength: Ultimate (UTS), MPa 170
390

Thermal Properties

Latent Heat of Fusion, J/g 130
310
Melting Completion (Liquidus), °C 720
1350
Melting Onset (Solidus), °C 600
1300
Specific Heat Capacity, J/kg-K 280
450
Thermal Expansion, µm/m-K 19
11

Otherwise Unclassified Properties

Density, g/cm3 9.7
8.8
Embodied Carbon, kg CO2/kg material 59
10
Embodied Energy, MJ/kg 930
140

Common Calculations

Stiffness to Weight: Axial, points 4.7
12
Stiffness to Weight: Bending, points 15
22
Strength to Weight: Axial, points 4.9
12
Strength to Weight: Bending, points 7.0
14
Thermal Shock Resistance, points 7.7
14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 1.0
Copper (Cu), % 28.4 to 31.5
0 to 1.3
Iron (Fe), % 0
0 to 3.0
Manganese (Mn), % 0
0 to 1.5
Nickel (Ni), % 0
95 to 100
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 2.0
Silver (Ag), % 59 to 61
0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 9.5 to 10.5
0
Residuals, % 0 to 0.15
0