AWS BAg-18 vs. N09777 Nickel

AWS BAg-18 belongs to the otherwise unclassified metals classification, while N09777 nickel belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-18 and the bottom bar is N09777 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
200
Poisson's Ratio 0.36
0.29
Shear Modulus, GPa 30
77
Tensile Strength: Ultimate (UTS), MPa 170
580

Thermal Properties

Latent Heat of Fusion, J/g 130
300
Melting Completion (Liquidus), °C 720
1440
Melting Onset (Solidus), °C 600
1390
Specific Heat Capacity, J/kg-K 280
460
Thermal Expansion, µm/m-K 19
13

Otherwise Unclassified Properties

Density, g/cm3 9.7
8.1
Embodied Carbon, kg CO2/kg material 59
7.4
Embodied Energy, MJ/kg 930
100

Common Calculations

Stiffness to Weight: Axial, points 4.7
14
Stiffness to Weight: Bending, points 15
24
Strength to Weight: Axial, points 4.9
20
Strength to Weight: Bending, points 7.0
19
Thermal Shock Resistance, points 7.7
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.35
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
14 to 19
Copper (Cu), % 28.4 to 31.5
0
Iron (Fe), % 0
28.5 to 47.5
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
2.5 to 5.5
Nickel (Ni), % 0
34 to 42
Niobium (Nb), % 0
0 to 0.1
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 59 to 61
0
Sulfur (S), % 0
0 to 0.010
Tin (Sn), % 9.5 to 10.5
0
Titanium (Ti), % 0
2.0 to 3.0
Residuals, % 0 to 0.15
0