AWS BAg-21 vs. EN 1.0591 Cast Steel
AWS BAg-21 belongs to the otherwise unclassified metals classification, while EN 1.0591 cast steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is AWS BAg-21 and the bottom bar is EN 1.0591 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 85 | |
190 |
Poisson's Ratio | 0.36 | |
0.29 |
Shear Modulus, GPa | 31 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 150 | |
620 |
Thermal Properties
Latent Heat of Fusion, J/g | 140 | |
250 |
Melting Completion (Liquidus), °C | 800 | |
1470 |
Melting Onset (Solidus), °C | 690 | |
1430 |
Specific Heat Capacity, J/kg-K | 280 | |
470 |
Thermal Expansion, µm/m-K | 19 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 9.8 | |
7.9 |
Embodied Energy, MJ/kg | 970 | |
18 |
Common Calculations
Stiffness to Weight: Axial, points | 4.8 | |
13 |
Stiffness to Weight: Bending, points | 15 | |
24 |
Strength to Weight: Axial, points | 4.2 | |
22 |
Strength to Weight: Bending, points | 6.4 | |
20 |
Thermal Shock Resistance, points | 6.6 | |
20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % | 27.5 to 29.5 | |
0 |
Iron (Fe), % | 0 | |
99.935 to 100 |
Nickel (Ni), % | 2.0 to 3.0 | |
0 |
Phosphorus (P), % | 0 | |
0 to 0.035 |
Silver (Ag), % | 62 to 64 | |
0 |
Sulfur (S), % | 0 | |
0 to 0.030 |
Tin (Sn), % | 5.0 to 7.0 | |
0 |
Residuals, % | 0 to 0.15 | |
0 |