AWS BAg-21 vs. EN 1.3961 Alloy

AWS BAg-21 belongs to the otherwise unclassified metals classification, while EN 1.3961 alloy belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-21 and the bottom bar is EN 1.3961 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 85
190
Poisson's Ratio 0.36
0.3
Shear Modulus, GPa 31
72
Tensile Strength: Ultimate (UTS), MPa 150
450

Thermal Properties

Latent Heat of Fusion, J/g 140
270
Melting Completion (Liquidus), °C 800
1430
Melting Onset (Solidus), °C 690
1390
Specific Heat Capacity, J/kg-K 280
460
Thermal Expansion, µm/m-K 19
1.3

Otherwise Unclassified Properties

Density, g/cm3 9.8
8.2
Embodied Energy, MJ/kg 970
66

Common Calculations

Stiffness to Weight: Axial, points 4.8
13
Stiffness to Weight: Bending, points 15
23
Strength to Weight: Axial, points 4.2
15
Strength to Weight: Bending, points 6.4
16
Thermal Shock Resistance, points 6.6
130

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
0 to 0.25
Copper (Cu), % 27.5 to 29.5
0
Iron (Fe), % 0
60.7 to 65
Manganese (Mn), % 0
0 to 0.5
Molybdenum (Mo), % 0
0 to 1.0
Nickel (Ni), % 2.0 to 3.0
35 to 37
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 62 to 64
0
Sulfur (S), % 0
0 to 0.020
Tin (Sn), % 5.0 to 7.0
0
Residuals, % 0 to 0.15
0