AWS BAg-21 vs. EN 1.4530 Stainless Steel

AWS BAg-21 belongs to the otherwise unclassified metals classification, while EN 1.4530 stainless steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-21 and the bottom bar is EN 1.4530 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 85
200
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 31
76
Tensile Strength: Ultimate (UTS), MPa 150
1030 to 1370

Thermal Properties

Latent Heat of Fusion, J/g 140
270
Melting Completion (Liquidus), °C 800
1460
Melting Onset (Solidus), °C 690
1410
Specific Heat Capacity, J/kg-K 280
470
Thermal Expansion, µm/m-K 19
11

Otherwise Unclassified Properties

Density, g/cm3 9.8
7.9
Embodied Energy, MJ/kg 970
46

Common Calculations

Stiffness to Weight: Axial, points 4.8
14
Stiffness to Weight: Bending, points 15
25
Strength to Weight: Axial, points 4.2
36 to 48
Strength to Weight: Bending, points 6.4
29 to 35
Thermal Shock Resistance, points 6.6
35 to 47

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0.6 to 0.8
Carbon (C), % 0
0 to 0.015
Chromium (Cr), % 0
11.5 to 12.5
Copper (Cu), % 27.5 to 29.5
0
Iron (Fe), % 0
74.4 to 77.3
Manganese (Mn), % 0
0 to 0.1
Molybdenum (Mo), % 0
1.9 to 2.2
Nickel (Ni), % 2.0 to 3.0
8.5 to 9.5
Nitrogen (N), % 0
0 to 0.010
Phosphorus (P), % 0
0 to 0.010
Silicon (Si), % 0
0 to 0.1
Silver (Ag), % 62 to 64
0
Sulfur (S), % 0
0 to 0.0050
Tin (Sn), % 5.0 to 7.0
0
Titanium (Ti), % 0
0.28 to 0.37
Residuals, % 0 to 0.15
0