AWS BAg-21 vs. EN 1.4640 Stainless Steel

AWS BAg-21 belongs to the otherwise unclassified metals classification, while EN 1.4640 stainless steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-21 and the bottom bar is EN 1.4640 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 85
200
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 31
77
Tensile Strength: Ultimate (UTS), MPa 150
620 to 650

Thermal Properties

Latent Heat of Fusion, J/g 140
280
Melting Completion (Liquidus), °C 800
1420
Melting Onset (Solidus), °C 690
1380
Specific Heat Capacity, J/kg-K 280
480
Thermal Expansion, µm/m-K 19
16

Otherwise Unclassified Properties

Density, g/cm3 9.8
7.8
Embodied Energy, MJ/kg 970
40

Common Calculations

Stiffness to Weight: Axial, points 4.8
14
Stiffness to Weight: Bending, points 15
25
Strength to Weight: Axial, points 4.2
22 to 23
Strength to Weight: Bending, points 6.4
21
Thermal Shock Resistance, points 6.6
14 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.030 to 0.080
Chromium (Cr), % 0
18 to 19
Copper (Cu), % 27.5 to 29.5
1.3 to 2.0
Iron (Fe), % 0
67.4 to 73.6
Manganese (Mn), % 0
1.5 to 4.0
Nickel (Ni), % 2.0 to 3.0
5.5 to 6.9
Nitrogen (N), % 0
0.030 to 0.11
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 62 to 64
0
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 5.0 to 7.0
0
Residuals, % 0 to 0.15
0