AWS BAg-21 vs. EN 1.4910 Stainless Steel

AWS BAg-21 belongs to the otherwise unclassified metals classification, while EN 1.4910 stainless steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-21 and the bottom bar is EN 1.4910 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 85
200
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 31
78
Tensile Strength: Ultimate (UTS), MPa 150
650

Thermal Properties

Latent Heat of Fusion, J/g 140
290
Melting Completion (Liquidus), °C 800
1440
Melting Onset (Solidus), °C 690
1400
Specific Heat Capacity, J/kg-K 280
470
Thermal Expansion, µm/m-K 19
16

Otherwise Unclassified Properties

Density, g/cm3 9.8
7.9
Embodied Energy, MJ/kg 970
54

Common Calculations

Stiffness to Weight: Axial, points 4.8
14
Stiffness to Weight: Bending, points 15
25
Strength to Weight: Axial, points 4.2
23
Strength to Weight: Bending, points 6.4
21
Thermal Shock Resistance, points 6.6
14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Boron (B), % 0
0.0015 to 0.0050
Carbon (C), % 0
0 to 0.040
Chromium (Cr), % 0
16 to 18
Copper (Cu), % 27.5 to 29.5
0
Iron (Fe), % 0
62 to 69.9
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 2.0 to 3.0
12 to 14
Nitrogen (N), % 0
0.1 to 0.18
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
0 to 0.75
Silver (Ag), % 62 to 64
0
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 5.0 to 7.0
0
Residuals, % 0 to 0.15
0