AWS BAg-21 vs. EN 1.5536 Steel

AWS BAg-21 belongs to the otherwise unclassified metals classification, while EN 1.5536 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-21 and the bottom bar is EN 1.5536 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 85
190
Poisson's Ratio 0.36
0.29
Shear Modulus, GPa 31
73
Tensile Strength: Ultimate (UTS), MPa 150
460 to 1600

Thermal Properties

Latent Heat of Fusion, J/g 140
250
Melting Completion (Liquidus), °C 800
1460
Melting Onset (Solidus), °C 690
1420
Specific Heat Capacity, J/kg-K 280
470
Thermal Expansion, µm/m-K 19
13

Otherwise Unclassified Properties

Density, g/cm3 9.8
7.8
Embodied Energy, MJ/kg 970
19

Common Calculations

Stiffness to Weight: Axial, points 4.8
13
Stiffness to Weight: Bending, points 15
24
Strength to Weight: Axial, points 4.2
16 to 57
Strength to Weight: Bending, points 6.4
17 to 39
Thermal Shock Resistance, points 6.6
14 to 47

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0
0.25 to 0.3
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 27.5 to 29.5
0 to 0.25
Iron (Fe), % 0
97.6 to 98.7
Manganese (Mn), % 0
0.9 to 1.2
Nickel (Ni), % 2.0 to 3.0
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0.15 to 0.3
Silver (Ag), % 62 to 64
0
Sulfur (S), % 0
0 to 0.025
Tin (Sn), % 5.0 to 7.0
0
Residuals, % 0 to 0.15
0