AWS BAg-21 vs. EN 1.7367 Steel

AWS BAg-21 belongs to the otherwise unclassified metals classification, while EN 1.7367 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-21 and the bottom bar is EN 1.7367 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 85
190
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 31
75
Tensile Strength: Ultimate (UTS), MPa 150
670

Thermal Properties

Latent Heat of Fusion, J/g 140
270
Melting Completion (Liquidus), °C 800
1460
Melting Onset (Solidus), °C 690
1420
Specific Heat Capacity, J/kg-K 280
470
Thermal Expansion, µm/m-K 19
13

Otherwise Unclassified Properties

Density, g/cm3 9.8
7.8
Embodied Energy, MJ/kg 970
37

Common Calculations

Stiffness to Weight: Axial, points 4.8
14
Stiffness to Weight: Bending, points 15
25
Strength to Weight: Axial, points 4.2
24
Strength to Weight: Bending, points 6.4
22
Thermal Shock Resistance, points 6.6
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.020
Carbon (C), % 0
0.080 to 0.12
Chromium (Cr), % 0
8.0 to 9.5
Copper (Cu), % 27.5 to 29.5
0
Iron (Fe), % 0
87.3 to 90.3
Manganese (Mn), % 0
0.3 to 0.6
Molybdenum (Mo), % 0
0.85 to 1.1
Nickel (Ni), % 2.0 to 3.0
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.2 to 0.5
Silver (Ag), % 62 to 64
0
Sulfur (S), % 0
0 to 0.010
Tin (Sn), % 5.0 to 7.0
0
Titanium (Ti), % 0
0 to 0.010
Vanadium (V), % 0
0.18 to 0.25
Zirconium (Zr), % 0
0 to 0.010
Residuals, % 0 to 0.15
0