AWS BAg-21 vs. S35140 Stainless Steel

AWS BAg-21 belongs to the otherwise unclassified metals classification, while S35140 stainless steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-21 and the bottom bar is S35140 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 85
200
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 31
78
Tensile Strength: Ultimate (UTS), MPa 150
690

Thermal Properties

Latent Heat of Fusion, J/g 140
300
Melting Completion (Liquidus), °C 800
1420
Melting Onset (Solidus), °C 690
1370
Specific Heat Capacity, J/kg-K 280
470
Thermal Expansion, µm/m-K 19
16

Otherwise Unclassified Properties

Density, g/cm3 9.8
8.0
Embodied Energy, MJ/kg 970
78

Common Calculations

Stiffness to Weight: Axial, points 4.8
14
Stiffness to Weight: Bending, points 15
24
Strength to Weight: Axial, points 4.2
24
Strength to Weight: Bending, points 6.4
22
Thermal Shock Resistance, points 6.6
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.1
Chromium (Cr), % 0
20 to 22
Copper (Cu), % 27.5 to 29.5
0
Iron (Fe), % 0
44.1 to 52.7
Manganese (Mn), % 0
1.0 to 3.0
Molybdenum (Mo), % 0
1.0 to 2.0
Nickel (Ni), % 2.0 to 3.0
25 to 27
Niobium (Nb), % 0
0.25 to 0.75
Nitrogen (N), % 0
0.080 to 0.2
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0
0 to 0.75
Silver (Ag), % 62 to 64
0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 5.0 to 7.0
0
Residuals, % 0 to 0.15
0