AWS BAg-22 vs. ASTM A182 Grade F12 Class 1

AWS BAg-22 belongs to the otherwise unclassified metals classification, while ASTM A182 grade F12 class 1 belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-22 and the bottom bar is ASTM A182 grade F12 class 1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 96
190
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 36
73
Tensile Strength: Ultimate (UTS), MPa 140
470

Thermal Properties

Latent Heat of Fusion, J/g 150
250
Melting Completion (Liquidus), °C 700
1470
Melting Onset (Solidus), °C 680
1420
Specific Heat Capacity, J/kg-K 320
470
Thermal Expansion, µm/m-K 21
13

Otherwise Unclassified Properties

Density, g/cm3 9.0
7.9
Embodied Carbon, kg CO2/kg material 48
1.6
Embodied Energy, MJ/kg 760
21

Common Calculations

Stiffness to Weight: Axial, points 5.9
13
Stiffness to Weight: Bending, points 17
24
Strength to Weight: Axial, points 4.3
17
Strength to Weight: Bending, points 6.6
17
Thermal Shock Resistance, points 5.1
14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.050 to 0.15
Chromium (Cr), % 0
0.8 to 1.3
Copper (Cu), % 15 to 17
0
Iron (Fe), % 0
96.8 to 98.4
Manganese (Mn), % 7.0 to 8.0
0.3 to 0.6
Molybdenum (Mo), % 0
0.44 to 0.65
Nickel (Ni), % 4.0 to 5.0
0
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 48 to 50
0
Sulfur (S), % 0
0 to 0.045
Zinc (Zn), % 21 to 25
0
Residuals, % 0 to 0.15
0