AWS BAg-23 vs. Solder Alloy 811

Both AWS BAg-23 and solder alloy 811 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 15 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-23 and the bottom bar is solder alloy 811.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 90
52
Poisson's Ratio 0.36
0.35
Shear Modulus, GPa 33
19
Tensile Strength: Ultimate (UTS), MPa 170
53

Thermal Properties

Latent Heat of Fusion, J/g 130
63
Melting Completion (Liquidus), °C 970
200
Melting Onset (Solidus), °C 960
190
Specific Heat Capacity, J/kg-K 270
230
Thermal Expansion, µm/m-K 20
22

Otherwise Unclassified Properties

Density, g/cm3 10
7.3

Common Calculations

Stiffness to Weight: Axial, points 5.0
4.0
Stiffness to Weight: Bending, points 15
17
Strength to Weight: Axial, points 4.7
2.0
Strength to Weight: Bending, points 6.8
4.3
Thermal Shock Resistance, points 6.8
3.3

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
2.8 to 3.2
Cadmium (Cd), % 0
0 to 0.0020
Copper (Cu), % 0
0 to 0.050
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 13.9 to 16
0
Nickel (Ni), % 0
0 to 0.010
Silver (Ag), % 84 to 86
0 to 0.1
Tin (Sn), % 0
87.8 to 89.7
Zinc (Zn), % 0
7.5 to 8.5
Residuals, % 0 to 0.15
0