AWS BAg-6 vs. Z24311 Zinc

AWS BAg-6 belongs to the otherwise unclassified metals classification, while Z24311 zinc belongs to the zinc alloys. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is Z24311 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
87
Poisson's Ratio 0.34
0.25
Shear Modulus, GPa 33
35
Tensile Strength: Ultimate (UTS), MPa 160
140

Thermal Properties

Latent Heat of Fusion, J/g 140
110
Melting Completion (Liquidus), °C 770
410
Melting Onset (Solidus), °C 690
400
Specific Heat Capacity, J/kg-K 310
390
Thermal Expansion, µm/m-K 20
26

Otherwise Unclassified Properties

Density, g/cm3 9.3
6.6
Embodied Carbon, kg CO2/kg material 49
2.8
Embodied Energy, MJ/kg 770
53

Common Calculations

Stiffness to Weight: Axial, points 5.3
7.4
Stiffness to Weight: Bending, points 16
23
Strength to Weight: Axial, points 4.8
6.1
Strength to Weight: Bending, points 7.0
9.3
Thermal Shock Resistance, points 6.5
4.6

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0020
Cadmium (Cd), % 0
0 to 0.0050
Copper (Cu), % 33 to 35
0 to 0.0050
Iron (Fe), % 0
0 to 0.010
Lead (Pb), % 0
0.030 to 0.080
Magnesium (Mg), % 0
0 to 0.0015
Manganese (Mn), % 0
0 to 0.015
Silver (Ag), % 49 to 51
0
Titanium (Ti), % 0
0 to 0.020
Zinc (Zn), % 14 to 18
99.862 to 100
Residuals, % 0 to 0.15
0