AWS BMg-1 vs. EN 1.4596 Stainless Steel

AWS BMg-1 belongs to the magnesium alloys classification, while EN 1.4596 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS BMg-1 and the bottom bar is EN 1.4596 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 47
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 18
76
Tensile Strength: Ultimate (UTS), MPa 180
1030 to 1600

Thermal Properties

Latent Heat of Fusion, J/g 350
280
Maximum Temperature: Mechanical, °C 130
790
Melting Completion (Liquidus), °C 600
1450
Melting Onset (Solidus), °C 440
1410
Specific Heat Capacity, J/kg-K 980
470
Thermal Expansion, µm/m-K 26
11

Otherwise Unclassified Properties

Base Metal Price, % relative 12
15
Density, g/cm3 1.8
7.9
Embodied Carbon, kg CO2/kg material 22
3.5
Embodied Energy, MJ/kg 160
48
Embodied Water, L/kg 980
130

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 66
25
Strength to Weight: Axial, points 27
36 to 56
Strength to Weight: Bending, points 39
29 to 39
Thermal Shock Resistance, points 10
35 to 54

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 8.3 to 9.7
0.8 to 1.1
Beryllium (Be), % 0.00020 to 0.00080
0
Carbon (C), % 0
0 to 0.015
Chromium (Cr), % 0
11.5 to 12.5
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0 to 0.0050
73.4 to 76.4
Magnesium (Mg), % 86.1 to 89.8
0
Manganese (Mn), % 0.15 to 1.5
0 to 0.1
Molybdenum (Mo), % 0
1.9 to 2.2
Nickel (Ni), % 0 to 0.0050
9.2 to 10.2
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0
0 to 0.010
Silicon (Si), % 0 to 0.050
0 to 0.1
Sulfur (S), % 0
0 to 0.0050
Titanium (Ti), % 0
0.28 to 0.4
Zinc (Zn), % 1.7 to 2.3
0
Residuals, % 0 to 0.3
0