AWS BVAg-18 vs. 852.0 Aluminum

AWS BVAg-18 belongs to the otherwise unclassified metals classification, while 852.0 aluminum belongs to the aluminum alloys. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS BVAg-18 and the bottom bar is 852.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
70
Poisson's Ratio 0.36
0.33
Shear Modulus, GPa 30
26
Tensile Strength: Ultimate (UTS), MPa 180
200

Thermal Properties

Latent Heat of Fusion, J/g 140
370
Melting Completion (Liquidus), °C 720
640
Melting Onset (Solidus), °C 600
210
Specific Heat Capacity, J/kg-K 280
840
Thermal Expansion, µm/m-K 19
23

Otherwise Unclassified Properties

Density, g/cm3 9.7
3.2
Embodied Carbon, kg CO2/kg material 59
8.5
Embodied Energy, MJ/kg 930
160

Common Calculations

Stiffness to Weight: Axial, points 4.7
12
Stiffness to Weight: Bending, points 15
43
Strength to Weight: Axial, points 5.1
17
Strength to Weight: Bending, points 7.3
24
Thermal Shock Resistance, points 8.1
8.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
86.6 to 91.3
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 28.5 to 31.5
1.7 to 2.3
Iron (Fe), % 0
0 to 0.7
Lead (Pb), % 0 to 0.0020
0
Magnesium (Mg), % 0
0.6 to 0.9
Manganese (Mn), % 0
0 to 0.1
Nickel (Ni), % 0
0.9 to 1.5
Phosphorus (P), % 0 to 0.0020
0
Silicon (Si), % 0
0 to 0.4
Silver (Ag), % 59 to 61
0
Tin (Sn), % 9.5 to 10.5
5.5 to 7.0
Titanium (Ti), % 0
0 to 0.2
Zinc (Zn), % 0 to 0.0010
0
Residuals, % 0
0 to 0.3