AWS BVAg-18 vs. C41300 Brass

AWS BVAg-18 belongs to the otherwise unclassified metals classification, while C41300 brass belongs to the copper alloys. They have a modest 31% of their average alloy composition in common, which, by itself, doesn't mean much. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-18 and the bottom bar is C41300 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
110
Poisson's Ratio 0.36
0.33
Shear Modulus, GPa 30
42
Tensile Strength: Ultimate (UTS), MPa 180
300 to 630

Thermal Properties

Latent Heat of Fusion, J/g 140
200
Melting Completion (Liquidus), °C 720
1040
Melting Onset (Solidus), °C 600
1010
Specific Heat Capacity, J/kg-K 280
380
Thermal Expansion, µm/m-K 19
18

Otherwise Unclassified Properties

Density, g/cm3 9.7
8.7
Embodied Carbon, kg CO2/kg material 59
2.7
Embodied Energy, MJ/kg 930
44

Common Calculations

Stiffness to Weight: Axial, points 4.7
7.2
Stiffness to Weight: Bending, points 15
18
Strength to Weight: Axial, points 5.1
9.6 to 20
Strength to Weight: Bending, points 7.3
11 to 19
Thermal Shock Resistance, points 8.1
11 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 28.5 to 31.5
89 to 93
Iron (Fe), % 0
0 to 0.050
Lead (Pb), % 0 to 0.0020
0 to 0.1
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 59 to 61
0
Tin (Sn), % 9.5 to 10.5
0.7 to 1.3
Zinc (Zn), % 0 to 0.0010
5.1 to 10.3
Residuals, % 0
0 to 0.5