AWS BVAg-18 vs. N08026 Nickel

AWS BVAg-18 belongs to the otherwise unclassified metals classification, while N08026 nickel belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-18 and the bottom bar is N08026 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
200
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 30
80
Tensile Strength: Ultimate (UTS), MPa 180
620

Thermal Properties

Latent Heat of Fusion, J/g 140
310
Melting Completion (Liquidus), °C 720
1430
Melting Onset (Solidus), °C 600
1380
Specific Heat Capacity, J/kg-K 280
460
Thermal Expansion, µm/m-K 19
15

Otherwise Unclassified Properties

Density, g/cm3 9.7
8.2
Embodied Carbon, kg CO2/kg material 59
7.2
Embodied Energy, MJ/kg 930
98

Common Calculations

Stiffness to Weight: Axial, points 4.7
14
Stiffness to Weight: Bending, points 15
24
Strength to Weight: Axial, points 5.1
21
Strength to Weight: Bending, points 7.3
20
Thermal Shock Resistance, points 8.1
15

Alloy Composition

Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0 to 0.030
Chromium (Cr), % 0
22 to 26
Copper (Cu), % 28.5 to 31.5
2.0 to 4.0
Iron (Fe), % 0
24.4 to 37.9
Lead (Pb), % 0 to 0.0020
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
5.0 to 6.7
Nickel (Ni), % 0
33 to 37.2
Nitrogen (N), % 0
0.1 to 0.16
Phosphorus (P), % 0 to 0.0020
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 59 to 61
0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 9.5 to 10.5
0
Zinc (Zn), % 0 to 0.0010
0