AWS BVAg-32 vs. Solder Alloy 501

Both AWS BVAg-32 and solder alloy 501 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 15 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-32 and the bottom bar is solder alloy 501.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
51
Poisson's Ratio 0.37
0.36
Shear Modulus, GPa 34
19
Tensile Strength: Ultimate (UTS), MPa 180
29

Thermal Properties

Latent Heat of Fusion, J/g 140
60
Melting Completion (Liquidus), °C 950
230
Melting Onset (Solidus), °C 900
220
Specific Heat Capacity, J/kg-K 270
220
Thermal Expansion, µm/m-K 17
22

Otherwise Unclassified Properties

Density, g/cm3 11
7.3

Common Calculations

Stiffness to Weight: Axial, points 4.9
3.8
Stiffness to Weight: Bending, points 14
17
Strength to Weight: Axial, points 4.7
1.1
Strength to Weight: Bending, points 6.7
2.9
Thermal Shock Resistance, points 8.0
1.9

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.060
Cadmium (Cd), % 0 to 0.0010
0 to 0.0020
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 20 to 22
0.5 to 0.9
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0 to 0.0020
0 to 0.070
Nickel (Ni), % 0
0 to 0.010
Palladium (Pd), % 23 to 27
0
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 53 to 55
0.2 to 0.4
Tin (Sn), % 0
98.3 to 99.3
Zinc (Zn), % 0 to 0.0010
0 to 0.0010