AWS E209 vs. ASTM A182 Grade F22V

Both AWS E209 and ASTM A182 grade F22V are iron alloys. They have 62% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS E209 and the bottom bar is ASTM A182 grade F22V.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
21
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
74
Tensile Strength: Ultimate (UTS), MPa 770
670

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1370
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 14
13

Otherwise Unclassified Properties

Base Metal Price, % relative 21
4.2
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.4
2.5
Embodied Energy, MJ/kg 63
35
Embodied Water, L/kg 180
61

Common Calculations

PREN (Pitting Resistance) 33
5.6
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
24
Strength to Weight: Bending, points 24
22
Thermal Shock Resistance, points 19
19

Alloy Composition

Boron (B), % 0
0 to 0.0020
Calcium (Ca), % 0
0 to 0.015
Carbon (C), % 0 to 0.060
0.11 to 0.15
Chromium (Cr), % 20.5 to 24
2.0 to 2.5
Copper (Cu), % 0 to 0.75
0 to 0.2
Iron (Fe), % 51.5 to 64.3
94.6 to 96.4
Manganese (Mn), % 4.0 to 7.0
0.3 to 0.6
Molybdenum (Mo), % 1.5 to 3.0
0.9 to 1.1
Nickel (Ni), % 9.5 to 12
0 to 0.25
Niobium (Nb), % 0
0 to 0.070
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 0 to 1.0
0 to 0.1
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0.1 to 0.3
0.25 to 0.35