AWS E2594 vs. EN 1.7106 Steel

Both AWS E2594 and EN 1.7106 steel are iron alloys. They have 61% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS E2594 and the bottom bar is EN 1.7106 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
72
Tensile Strength: Ultimate (UTS), MPa 850
660 to 2020

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
46
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 22
2.1
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 4.3
1.5
Embodied Energy, MJ/kg 60
20
Embodied Water, L/kg 190
47

Common Calculations

Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
24 to 73
Strength to Weight: Bending, points 25
22 to 46
Thermal Diffusivity, mm2/s 4.3
13
Thermal Shock Resistance, points 21
20 to 61

Alloy Composition

Carbon (C), % 0 to 0.040
0.52 to 0.6
Chromium (Cr), % 24 to 27
0.2 to 0.45
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 53.8 to 63.8
95.9 to 97
Manganese (Mn), % 0.5 to 2.0
0.7 to 1.0
Molybdenum (Mo), % 3.5 to 4.5
0
Nickel (Ni), % 8.0 to 10.5
0
Nitrogen (N), % 0.2 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
1.6 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.025