AWS E308L vs. EN 1.0116 Steel

Both AWS E308L and EN 1.0116 steel are iron alloys. They have 69% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E308L and the bottom bar is EN 1.0116 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
23
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 580
380

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
49
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 16
2.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.2
1.4
Embodied Energy, MJ/kg 46
19
Embodied Water, L/kg 150
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
13
Strength to Weight: Bending, points 20
15
Thermal Diffusivity, mm2/s 4.1
13
Thermal Shock Resistance, points 15
12

Alloy Composition

Carbon (C), % 0 to 0.040
0 to 0.17
Chromium (Cr), % 18 to 21
0 to 0.3
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 62.9 to 72.5
97.1 to 100
Manganese (Mn), % 0.5 to 2.5
0 to 1.4
Molybdenum (Mo), % 0 to 0.75
0 to 0.080
Nickel (Ni), % 9.0 to 11
0 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.55
Sulfur (S), % 0 to 0.030
0 to 0.035