AWS E312 vs. AWS ER80S-B6

Both AWS E312 and AWS ER80S-B6 are iron alloys. They have 65% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E312 and the bottom bar is AWS ER80S-B6.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
19
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
74
Tensile Strength: Ultimate (UTS), MPa 740
620

Thermal Properties

Latent Heat of Fusion, J/g 310
260
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1360
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 15
13

Otherwise Unclassified Properties

Base Metal Price, % relative 20
4.7
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.6
1.8
Embodied Energy, MJ/kg 52
24
Embodied Water, L/kg 200
71

Common Calculations

PREN (Pitting Resistance) 31
7.1
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
22
Strength to Weight: Bending, points 24
21
Thermal Shock Resistance, points 18
18

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.1
Chromium (Cr), % 28 to 32
4.5 to 6.0
Copper (Cu), % 0 to 0.75
0 to 0.35
Iron (Fe), % 52.3 to 63.5
90.6 to 94.7
Manganese (Mn), % 0.5 to 2.5
0.4 to 0.7
Molybdenum (Mo), % 0 to 0.75
0.45 to 0.65
Nickel (Ni), % 8.0 to 10.5
0 to 0.6
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.025
Residuals, % 0
0 to 0.5