AWS E312 vs. EN 1.0033 Steel

Both AWS E312 and EN 1.0033 steel are iron alloys. They have 59% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS E312 and the bottom bar is EN 1.0033 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
17 to 32
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 740
300 to 330

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1410
1470
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 15
12

Otherwise Unclassified Properties

Base Metal Price, % relative 20
1.8
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.6
1.4
Embodied Energy, MJ/kg 52
18
Embodied Water, L/kg 200
45

Common Calculations

Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
10 to 12
Strength to Weight: Bending, points 24
13 to 14
Thermal Shock Resistance, points 18
9.4 to 10

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.11
Chromium (Cr), % 28 to 32
0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 52.3 to 63.5
98.8 to 100
Manganese (Mn), % 0.5 to 2.5
0 to 0.7
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 8.0 to 10.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.045