AWS E312 vs. EN 1.3539 Steel

Both AWS E312 and EN 1.3539 steel are iron alloys. They have 62% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E312 and the bottom bar is EN 1.3539 steel.

AWS E312 (W31310) Weld Metal EN 1.3539 (100CrMnMoSi8-4-6) Through-Hardening Bearing Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.27
Poisson's Ratio		0.29

Shear Modulus, GPa		80
Shear Modulus, GPa		73

Tensile Strength: Ultimate (UTS), MPa		740
Tensile Strength: Ultimate (UTS), MPa		670

Thermal Properties

Latent Heat of Fusion, J/g		310
Latent Heat of Fusion, J/g		260

Melting Completion (Liquidus), °C		1410
Melting Completion (Liquidus), °C		1450

Melting Onset (Solidus), °C		1360
Melting Onset (Solidus), °C		1410

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		15
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Base Metal Price, % relative		20
Base Metal Price, % relative		3.2

Density, g/cm³		7.7
Density, g/cm³		7.8

Embodied Carbon, kg CO₂/kg material		3.6
Embodied Carbon, kg CO₂/kg material		1.7

Embodied Energy, MJ/kg		52
Embodied Energy, MJ/kg		22

Embodied Water, L/kg		200
Embodied Water, L/kg		57

Common Calculations

PREN (Pitting Resistance)		31
PREN (Pitting Resistance)		3.8

Stiffness to Weight: Axial, points		15
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		27
Strength to Weight: Axial, points		24

Strength to Weight: Bending, points		24
Strength to Weight: Bending, points		22

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		20

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.050

Carbon (C), %		0 to 0.15
Carbon (C), %		0.93 to 1.1

Chromium (Cr), %		28 to 32
Chromium (Cr), %		1.8 to 2.1

Copper (Cu), %		0 to 0.75
Copper (Cu), %		0 to 0.3

Iron (Fe), %		52.3 to 63.5
Iron (Fe), %		95.2 to 96.5

Manganese (Mn), %		0.5 to 2.5
Manganese (Mn), %		0.8 to 1.1

Molybdenum (Mo), %		0 to 0.75
Molybdenum (Mo), %		0.5 to 0.6

Nickel (Ni), %		8.0 to 10.5
Nickel (Ni), %		0

Oxygen (O), %		0
Oxygen (O), %		0 to 0.0015

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.025

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0.4 to 0.6

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030