AWS E312 vs. EN 1.4313 Stainless Steel

Both AWS E312 and EN 1.4313 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS E312 and the bottom bar is EN 1.4313 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
12 to 17
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 740
750 to 1000

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Melting Completion (Liquidus), °C 1410
1450
Melting Onset (Solidus), °C 1360
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 15
10

Otherwise Unclassified Properties

Base Metal Price, % relative 20
10
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.6
2.4
Embodied Energy, MJ/kg 52
34
Embodied Water, L/kg 200
110

Common Calculations

PREN (Pitting Resistance) 31
15
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
27 to 36
Strength to Weight: Bending, points 24
23 to 28
Thermal Shock Resistance, points 18
27 to 36

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.050
Chromium (Cr), % 28 to 32
12 to 14
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 52.3 to 63.5
78.5 to 84.2
Manganese (Mn), % 0.5 to 2.5
0 to 1.5
Molybdenum (Mo), % 0 to 0.75
0.3 to 0.7
Nickel (Ni), % 8.0 to 10.5
3.5 to 4.5
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.7
Sulfur (S), % 0 to 0.030
0 to 0.015