AWS E312 vs. EN 1.4482 Stainless Steel

Both AWS E312 and EN 1.4482 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS E312 and the bottom bar is EN 1.4482 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
34
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 740
770 to 800

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Melting Completion (Liquidus), °C 1410
1420
Melting Onset (Solidus), °C 1360
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 15
13

Otherwise Unclassified Properties

Base Metal Price, % relative 20
12
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 3.6
2.7
Embodied Energy, MJ/kg 52
38
Embodied Water, L/kg 200
150

Common Calculations

PREN (Pitting Resistance) 31
24
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
28 to 29
Strength to Weight: Bending, points 24
24 to 25
Thermal Shock Resistance, points 18
21 to 22

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.030
Chromium (Cr), % 28 to 32
19.5 to 21.5
Copper (Cu), % 0 to 0.75
0 to 1.0
Iron (Fe), % 52.3 to 63.5
66.1 to 74.9
Manganese (Mn), % 0.5 to 2.5
4.0 to 6.0
Molybdenum (Mo), % 0 to 0.75
0.1 to 0.6
Nickel (Ni), % 8.0 to 10.5
1.5 to 3.5
Nitrogen (N), % 0
0.050 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030