AWS E312 vs. EN 1.4507 Stainless Steel

Both AWS E312 and EN 1.4507 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS E312 and the bottom bar is EN 1.4507 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
25
Poisson's Ratio 0.27
0.27
Shear Modulus, GPa 80
80
Tensile Strength: Ultimate (UTS), MPa 740
840

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Melting Completion (Liquidus), °C 1410
1440
Melting Onset (Solidus), °C 1360
1390
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 15
13

Otherwise Unclassified Properties

Base Metal Price, % relative 20
21
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.6
4.0
Embodied Energy, MJ/kg 52
55
Embodied Water, L/kg 200
180

Common Calculations

PREN (Pitting Resistance) 31
41
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
30
Strength to Weight: Bending, points 24
25
Thermal Shock Resistance, points 18
23

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.030
Chromium (Cr), % 28 to 32
24 to 26
Copper (Cu), % 0 to 0.75
1.0 to 2.5
Iron (Fe), % 52.3 to 63.5
56.4 to 65.8
Manganese (Mn), % 0.5 to 2.5
0 to 2.0
Molybdenum (Mo), % 0 to 0.75
3.0 to 4.0
Nickel (Ni), % 8.0 to 10.5
6.0 to 8.0
Nitrogen (N), % 0
0.2 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.7
Sulfur (S), % 0 to 0.030
0 to 0.015