AWS E312 vs. EN 1.6570 Steel

Both AWS E312 and EN 1.6570 steel are iron alloys. They have 63% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS E312 and the bottom bar is EN 1.6570 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
11 to 17
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 740
910 to 1130

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 15
13

Otherwise Unclassified Properties

Base Metal Price, % relative 20
3.9
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.6
1.7
Embodied Energy, MJ/kg 52
23
Embodied Water, L/kg 200
56

Common Calculations

PREN (Pitting Resistance) 31
2.5
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
32 to 40
Strength to Weight: Bending, points 24
27 to 31
Thermal Shock Resistance, points 18
27 to 33

Alloy Composition

Carbon (C), % 0 to 0.15
0.28 to 0.35
Chromium (Cr), % 28 to 32
1.0 to 1.4
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 52.3 to 63.5
94 to 96.2
Manganese (Mn), % 0.5 to 2.5
0.6 to 1.0
Molybdenum (Mo), % 0 to 0.75
0.3 to 0.5
Nickel (Ni), % 8.0 to 10.5
1.6 to 2.1
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.015