AWS E312 vs. EN 1.8522 Steel

Both AWS E312 and EN 1.8522 steel are iron alloys. They have 62% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E312 and the bottom bar is EN 1.8522 steel.

AWS E312 (W31310) Weld Metal EN 1.8522 (33CrMoV12-9) High-Temperature Bearing Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.27
Poisson's Ratio		0.29

Shear Modulus, GPa		80
Shear Modulus, GPa		74

Tensile Strength: Ultimate (UTS), MPa		740
Tensile Strength: Ultimate (UTS), MPa		730 to 1250

Thermal Properties

Latent Heat of Fusion, J/g		310
Latent Heat of Fusion, J/g		260

Melting Completion (Liquidus), °C		1410
Melting Completion (Liquidus), °C		1460

Melting Onset (Solidus), °C		1360
Melting Onset (Solidus), °C		1420

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		15
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Base Metal Price, % relative		20
Base Metal Price, % relative		4.2

Density, g/cm³		7.7
Density, g/cm³		7.8

Embodied Carbon, kg CO₂/kg material		3.6
Embodied Carbon, kg CO₂/kg material		2.2

Embodied Energy, MJ/kg		52
Embodied Energy, MJ/kg		31

Embodied Water, L/kg		200
Embodied Water, L/kg		63

Common Calculations

PREN (Pitting Resistance)		31
PREN (Pitting Resistance)		6.2

Stiffness to Weight: Axial, points		15
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		27
Strength to Weight: Axial, points		26 to 44

Strength to Weight: Bending, points		24
Strength to Weight: Bending, points		23 to 33

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		21 to 36

Alloy Composition

Carbon (C), %		0 to 0.15
Carbon (C), %		0.29 to 0.36

Chromium (Cr), %		28 to 32
Chromium (Cr), %		2.8 to 3.3

Copper (Cu), %		0 to 0.75
Copper (Cu), %		0 to 0.1

Iron (Fe), %		52.3 to 63.5
Iron (Fe), %		93.7 to 96

Manganese (Mn), %		0.5 to 2.5
Manganese (Mn), %		0.4 to 0.7

Molybdenum (Mo), %		0 to 0.75
Molybdenum (Mo), %		0.7 to 1.2

Nickel (Ni), %		8.0 to 10.5
Nickel (Ni), %		0 to 0.3

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.025

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0 to 0.4

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.035

Vanadium (V), %		0
Vanadium (V), %		0.15 to 0.25