MakeItFrom.com
Menu (ESC)

AWS E312 vs. SAE-AISI T15 Steel

Both AWS E312 and SAE-AISI T15 steel are iron alloys. They have 64% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS E312 and the bottom bar is SAE-AISI T15 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 740
830 to 2240

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1410
1690
Melting Onset (Solidus), °C 1360
1640
Specific Heat Capacity, J/kg-K 480
430
Thermal Expansion, µm/m-K 15
12

Otherwise Unclassified Properties

Base Metal Price, % relative 20
43
Density, g/cm3 7.7
8.7
Embodied Carbon, kg CO2/kg material 3.6
16
Embodied Energy, MJ/kg 52
250
Embodied Water, L/kg 200
140

Common Calculations

PREN (Pitting Resistance) 31
27
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 27
26 to 71
Strength to Weight: Bending, points 24
22 to 43
Thermal Shock Resistance, points 18
26 to 70

Alloy Composition

Carbon (C), % 0 to 0.15
1.5 to 1.6
Chromium (Cr), % 28 to 32
3.8 to 5.0
Cobalt (Co), % 0
4.8 to 5.3
Copper (Cu), % 0 to 0.75
0 to 0.25
Iron (Fe), % 52.3 to 63.5
67.5 to 73.5
Manganese (Mn), % 0.5 to 2.5
0.15 to 0.4
Molybdenum (Mo), % 0 to 0.75
0 to 1.0
Nickel (Ni), % 8.0 to 10.5
0 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0.15 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
11.8 to 13
Vanadium (V), % 0
4.5 to 5.3