AWS E312 vs. S20161 Stainless Steel

Both AWS E312 and S20161 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS E312 and the bottom bar is S20161 stainless steel.

AWS E312 (W31310) Weld Metal UNS S20161 Stainless Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		190

Elongation at Break, %		25
Elongation at Break, %		46

Poisson's Ratio		0.27
Poisson's Ratio		0.28

Shear Modulus, GPa		80
Shear Modulus, GPa		76

Tensile Strength: Ultimate (UTS), MPa		740
Tensile Strength: Ultimate (UTS), MPa		980

Thermal Properties

Latent Heat of Fusion, J/g		310
Latent Heat of Fusion, J/g		330

Melting Completion (Liquidus), °C		1410
Melting Completion (Liquidus), °C		1380

Melting Onset (Solidus), °C		1360
Melting Onset (Solidus), °C		1330

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		490

Thermal Expansion, µm/m-K		15
Thermal Expansion, µm/m-K		16

Otherwise Unclassified Properties

Base Metal Price, % relative		20
Base Metal Price, % relative		12

Density, g/cm³		7.7
Density, g/cm³		7.5

Embodied Carbon, kg CO₂/kg material		3.6
Embodied Carbon, kg CO₂/kg material		2.7

Embodied Energy, MJ/kg		52
Embodied Energy, MJ/kg		39

Embodied Water, L/kg		200
Embodied Water, L/kg		130

Common Calculations

PREN (Pitting Resistance)		31
PREN (Pitting Resistance)		19

Stiffness to Weight: Axial, points		15
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		26

Strength to Weight: Axial, points		27
Strength to Weight: Axial, points		36

Strength to Weight: Bending, points		24
Strength to Weight: Bending, points		29

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		22

Alloy Composition

Carbon (C), %		0 to 0.15
Carbon (C), %		0 to 0.15

Chromium (Cr), %		28 to 32
Chromium (Cr), %		15 to 18

Copper (Cu), %		0 to 0.75
Copper (Cu), %		0

Iron (Fe), %		52.3 to 63.5
Iron (Fe), %		65.6 to 73.9

Manganese (Mn), %		0.5 to 2.5
Manganese (Mn), %		4.0 to 6.0

Molybdenum (Mo), %		0 to 0.75
Molybdenum (Mo), %		0

Nickel (Ni), %		8.0 to 10.5
Nickel (Ni), %		4.0 to 6.0

Nitrogen (N), %		0
Nitrogen (N), %		0.080 to 0.2

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0 to 1.0
Silicon (Si), %		3.0 to 4.0

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.040