AWS E316H vs. AISI 410 Stainless Steel

Both AWS E316H and AISI 410 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS E316H and the bottom bar is AISI 410 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
16 to 22
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
76
Tensile Strength: Ultimate (UTS), MPa 580
520 to 770

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Melting Completion (Liquidus), °C 1440
1530
Melting Onset (Solidus), °C 1390
1480
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
30
Thermal Expansion, µm/m-K 14
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
7.0
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.0
1.9
Embodied Energy, MJ/kg 55
27
Embodied Water, L/kg 160
100

Common Calculations

PREN (Pitting Resistance) 27
13
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
19 to 28
Strength to Weight: Bending, points 20
19 to 24
Thermal Diffusivity, mm2/s 4.0
8.1
Thermal Shock Resistance, points 15
18 to 26

Alloy Composition

Carbon (C), % 0.040 to 0.080
0.080 to 0.15
Chromium (Cr), % 17 to 20
11.5 to 13.5
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 58.6 to 69.5
83.5 to 88.4
Manganese (Mn), % 0.5 to 2.5
0 to 1.0
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 11 to 14
0 to 0.75
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030